Whytheat C Castable
Being one of the leading company, we are able to provide supreme quality Whytheat - C Castable. The provided cement is mainly used to make statues & molds in various industries. Latest machines and techniques are used by our trained professionals to process the cement. Our vendors facilitate us with premium grade raw-materials, which are incorporated at the time of production process. To fulfill the diverse requirements of our clients, we offer the Whytheat - C Castable in many packaging sizes.
- Product: Whytheat C
- Product Class: Refractory
- Monolithic Type: 50 % Alumina Dense Castable
- Nature of Bond: Hydraulic
- Installation: Vibration Casting
General Properties
- Max. Service Temperature: 1500 c
- Maximum Grain Size: 5 Mm
- Water Required for Casting: 10.5 -11.5 %
CHEMICAL ANALYSIS, %
| RANGE | TYPICAL VALUE | TEST PROCEDURE |
Al2O3 | 48 52 | 50.5 | BIS 12107 Part 3 |
CaO | 4.2 4.9 | 4.50 | ASTM C 573 |
Fe2O3 | 0.8 1.5 | 1.20 | BIS 12107 Part 6 |
PHYSICAL PROPERTIES
| RANGE | TYPICAL VALUE | TEST PROCEDURE |
Dry density, g / cc after drying at 110 C / 24 hrs | 2.10 2.25 | 2.17 | BIS 10570 |
CCS, kg/cm2 after drying at 110 C / 24 hrs after heating at 1100 C / 3 hrs after heating at 1500 C / 3 hrs | 350 430 180 280 530 680 | 380 220 610 | BIS 10570 BIS 10570 BIS 10570 |
% Retained on maximum size | 0 5 | 1.0 | BIS 1528 Part 14 |
THERMAL PROPERTIES
| RANGE | TYPICAL VALUE | TEST PROCEDURE |
Refractoriness, Orton / C | | 30 / 1665 | BIS 1528 Part 1 |
PLC, % after heating at 1100 C / 3 hrs after heating at 1500 C / 3 hrs | (- 0.4) to (+0.2) (- 1.0) to (-2.5) | -0.15 -1.50 | BIS 10570 BIS 10570 |
- Packaging: 50 kg bags
- Delivery State: Dry
- Storage Life: Best till 9 months from the date of production, if stored in proper condition.
Note: The data are current production averages. They can not be used as limits for specification.
![]() |